PolyColor Dyes 56gr. can. -Special pigments for polyurethane
22,99 € IVA incl.
Polyurethane resinEasyFlo ClearIs a fast resin that has been specifically designed to add pigments and fillers in order to achieve the exact representation of the desired color or effect.
This resin has been formulated in a neutral color, therefore, a small amount of pigment will yield much more and vividly colored pieces will be achieved with the use of pigments PolyColor.
Offers a comfortable mix one-to-one ratio (1A:1B by volume).
Thanks to its neutral color, theEasyFlo Clearis ideal to create wood or marble effects thanks to our fillers, or to create an almost real metallic look by adding metallic fillers of bronze, copper or aluminum (cold casting)
Resin EasyFlo ClearHave a low viscosity and are perfectly suitable for pigments of the series PolyColor.However, these types of transparent resins arewill require a vacuum systemTo avoid the appearance of bubbles in the mixture.
EasyFlo Clear is slightly more sensitive to humidity than other EasyFlo products and is therefore more prone to air bubbles, so if you do not need transparency, it is better to use EasyFlo 60. The color of the polyurethane Part B may change color from batch to batch or may darken over time, but the performance of the product is not affected.
Product | Mixture A:B |
Working Time |
Curing Time |
Shore Hardness |
Color |
Mixture Viscosity |
Exothermic Peak |
Contraction |
EasyFlo 60 |
1A:1B(volume) 100A:90B (weight) |
2.5 min. | 15-30 min* |
65D |
White |
60 cP. |
110 ºC |
0.0041% |
EasyFlo 90 |
1A:1B(volume) 100A:90B(weight) |
5 min. | 60-120 min* |
70D |
White |
200 cP. |
80 ºC |
<0.001% |
EasyFlo 120 |
1A:1B(volume) 100A:90B(weight) |
2.5 min. | 15-30 min* |
65D |
White |
120 cP. |
93 ºC |
0.0065% |
EasyFlo Clear |
1A:1B(volume) 100A:85B(weight) |
2.5 min. | 15-30 min* |
72D |
Light amber |
110 cP. |
98 ºC |
0.0154% |
EasyFlo Black |
1A:1B(volume and weight) |
1.5 min. | 10-15 min* |
70D |
Black |
200 cP. |
121 ºC |
0.008% |
* Depending on the mass and ambient temperature