PlatSil FS-10 -Platinum Silicone-

PlatSil FS-10 -Platinum Silicone-

290040101
€42.00
50,82 € IVA incl.
  • Platinum Silicone (Addition) translucent.
  • Easy to use. Mixture 1A:1B
  • Shore Hardness: A13
  • Fast and High Strength
capacity
  • Kit of 900 gr.
  • Gallon Kit - (7.20Kgs)
  • 5 Gallon Kit - (36.28kgs)

 

The new Silicone FS-10From PolytekOffers truly exceptional performance like no platinum mold silicone has ever had before.

The FS-10From Polytekhas a time of cured very fast 20 to 25 minutes, but with a working time of about 8 minutes, always depending on the ambient temperature, which should be around 23 ºC

FST20

The ample working time allows cast silicone comfortably, as well as being perfect for apply it with a brush since it has a moment of gel before curing that does not sag.

All this with a incredible tear resistance, it is practically unbreakable when pulled during difficult demolding operations!

It is very easy to use as it is mixed in equal parts by weight or volume (1A:1B

Nature transparent of the cured silcona makes it a good option for the molds that need to be cut after curing, as the model is visible and the parting lines can be better determined. It is also very useful when making molds of complex parts to ensure that all hard-to-reach parts of the part are filled with the silicone. It is a silicone of casting, but it can be thickened or thixotroped withPlatThixTo be brushed.

PRECAUTIONS:

Contamination by sulfur (e.g., sulfur-based clays), amines, amine compounds (e.g., sulfur-based clays), amine compounds (e.g., sulfur tin, some silicone resins, cured polyester resin, some paints, and some silicone rubbers may inhibit surface curing of platinum-cured rubbers.

Product Mixture A:B
Working Time
Curing Time
Shore Hardness
Color

Mixture Viscosity

Specific volume
Contraction

PlatSil73-15

1A:1B by weight or volume 20 min. 4-5 hours

A15

Translucent White

2.500 cP.

25 in³/lb

Inappreciable

PlatSil73-20

1A:1B by weight or volume 5 min. 1 hour

A22

Translucent Blue

3,000 cP.

25 in³/lb

Inappreciable

PlatSil FS-10

1A:1B by weight or volume 8 min. 25 min.

A13

Translucent White

4.200 cP.

24.9 in³/lb

Inappreciable

PlatSilFS-20

1A:1B by weight or volume 8 min. 25 min.

A20

Translucent White

3.800 cP.

24.9 in³/lb

Inappreciable

lupa

PLATSIL FS20 BY JUAN VILLA

PLATSIL FS20 MASK IN PLATSIL FS20

NEILL GORTON USING PLATSILFS

Color
Translucent White
Working Time
8min
Curing Time
25min
Shore Hardness
A13
Volume Mixing Ratio
100A:100B
Mixed Weight Ratio
100A:100B