EASYCLEAR -Silicona de Estaño Translúcida-

EASYCLEAR -Translucent Tin Silicone - EASYCLEAR

201352101
€21.00
25,41 € IVA incl.
  • Silicone from tin for molds
  • Translucent color
  • Ideal for block and cutting molds and FX
  • Excellent price/performance ratio

capacity
  • Kit of 1 Kg.
  • Kit of 5 Kg.
  • Kit of 20 kg.

 

EASYCLEAR is atwo component (parts A and B) translucent siliconeelastomerthat cures at room temperature, the base (part A) has the appearance of atranslucent viscous liquid which, after theaddition of EASYCAT-20 catalyst (part B), transforms into anelastic material. It exhibits exceptional flowability and good workability.

EASYCLEAR is recommended for the application of molds for Plaster, Polyester Resin, Polyurethane Resin, Epoxy Resin, Fiberglass, Wax, Soap, Bronze, etc. casts.
As it is a soft silicone rubber with low viscosity, it is suitable for molds with complicated hollows that are difficult to demold.

Due to its translucency it is perfect for block molds or as a material for hyper-realistic parts.

INSTRUCTIONS:

1- Prepare the box for the mold and the original.

2- Set aside 100 parts of the base (Part A) and add 5 parts of catalyst (Part B) mix VERY well both parts until a homogeneous mixture is obtained.

3- Pour the silicone casting into the box or apply with a brush if it has been previously thixotropic .
NOTE: Normally low hardness silicone is used for molds of casting, since it allows a better demolding and thus does not damage the original .

Product

Proportion

Mixing ratio

Curing Time

Breaking Strength

Viscosity of the mixture

Working Time

Shore Hardness A

Tensile Strength

Color

EASYCLEAR

100:5

(5% catalyst)

4-5 hours 400% 13000 cps 20 min. 20 33 Kgf/cm Translucent

lupa

ONE-SIDED SILICONE MOLD


DOUBLE-SIDED SILICONE MOLD

MOULD WITH PINCEL by SIMBIOX


Color
Translucent
Working Time
20min
Curing Time
4-5horas
Shore Hardness
A20
Mixed Weight Ratio
100A:5B
Silicones
Condensation (Tin)
No reviews